CASE STUDIES | SPONGE-JET

PROJECT

Concrete Restoration at the Guggenheim Museum

After 50 years of exposure to the elements, the Frank Lloyd Wright-designed Guggenheim Museum on New York City’s 5th Avenue needed help.

The art museum’s exterior concrete rotunda wall, which corkscrews outward as the building gets taller, was beset by hundreds of cracks ranging from hairlines to those that exposed steel reinforcement bars buried in 5-inch-thick (12.7 cm) concrete. And that’s just what Guggenheim’s team of architects, engineers, and restoration experts could see! Who knew what else lay beneath 12 layers of coatings applied over the decades?

PROBLEM

 

 

Using laser scan imaging and ground penetrating radar to create a 3D view that included buried steel reinforcements, the team came up with a repair plan. But first, they had to remove 50,000 square feet (4,645 m²) of old coatings, and this presented a problem.

RESTORING CONCRETE WITH AN ARTIST'S TOUCH

    

Conventional sandblasting on concrete substrates kicks up respirable crystalline silica, known to cause lung cancer, silicosis, chronic obstructive pulmonary disease, and kidney disease according to U.S. Occupational Safety and Health Administration (OSHA). Even with dust containment, Guggenheim officials were concerned that conventional blasting might expose pedestrians, automobiles, and nearby high-profile residences to fine dust and other contaminants.

They needed a method to efficiently remove residual coatings and properly prepare for a new coating system—but with an artist’s touch—to only slightly abrade the existing substrate while minimizing airborne contaminants.

 

SOLUTION

 

 

Low Dust, Low Rebound

Micro Abrasion From Sponge-Jet

 

After an exhaustive test process involving a wide range of potential blast media and application methods, the Guggenheim restoration experts selected Sponge-Jet Sponge Media™, which is designed to provide dry, low-dust, low-rebound micro-abrasion. As the name implies, Sponge-Jet works by firing sponge-coated blast media at the substrate. Individual sponge-like granules strike the surface, remove coatings, and entrap up to 99 percent of what would otherwise become airborne contaminants. Spent granules are vacuumed, fed through a recycler to separate out abraded coatings, and reused.

Sponge-Jet Silver 120 Sponge Media™ was selected for speed of base-coatings removal and that it created a fine profile to which new coatings could adhere, but without altering the building’s original texture.

DRY MEDIA

Sponge-Jet’s Silver 120 (Sponge Media impregnated with 120-grit Aluminum Oxide) helped uncover more than one thousand cracks and damaged areas. In cases where significant concrete loss exposed reinforcement steel to the elements, Silver 120 was used to remove corrosion.

 

 

"The concrete surfaces could not be wet during the cleaning process because water would accelerate rusting of the reinforcing mesh just under the surface of the concrete,"

stated Andrew Wilson of the restoration contracting firm Nicholson & Galloway.

"Therefore a dry system needed to be used."

FINALLY

 Nicholson & Galloway and painting subcontractor H&S Environmental installed a 110-mil (2,794 micron), two-component elastomeric coating system to keep the Guggenheim Museum safe from water intrusion and accelerated damage from freeze/thaw cycles.

Nicholson & Galloway knows they made the right decision to partner with Sponge-Jet on the four-year, $29 million Guggenheim Museum project.

While traditional engineering controls for blasting with silica abrasives offer some benefit, the best way to safeguard workers and those nearby is to, “Replace crystalline silica materials with safer substitutes, whenever possible,” according to OSHA’s Crystalline Silica Exposure fact sheet. Sponge-Media is deemed “less toxic” by OSHA and limits up to 99 percent of dust at the source of generation.

"We were very happy with the system, particularly the low-dust aspect,” said Wilson.

PROJECT 

Removal of Salts, Grease, and Corrosion

from Food Processing Plant

Many food processing plants have used Sponge-Jet to avoid contaminating equipment while cleaning their facilities. At a food processing plant in Georgia, many different kinds of substrates were cleaned, from concrete and steel to conduit and galvanized pipe. Layers of rust, salts, grease, and flaking paint were removed without water or chemical cleaning - a requirement of the facility owner. 

HOW IT WORKS

SOLUTION